德國FISCHER便攜式電磁感應(yīng)鐵素體測試儀的特點：

• 在現(xiàn)場或?qū)嶒炇抑锌焖?、無損地測量鐵素體含量
• 測量范圍： 0.1 - 80% Fe 或 0.1 - 110 FN
• 可以以鐵素體百分比“%Fe”或是以鐵素體數(shù)“FN”作為測量單位
• 根據(jù) ISO 17655標(biāo)準(zhǔn)或“巴塞爾標(biāo)準(zhǔn)”進行測量
• 校準(zhǔn)用標(biāo)準(zhǔn)片可溯源到 TWI 二級標(biāo)準(zhǔn)，符合標(biāo)準(zhǔn)ISO 8249 以及 AWS A4.2M 的要求。
• 可以使用客戶自有的標(biāo)準(zhǔn)進行校準(zhǔn).

德國FISCHER便攜式電磁感應(yīng)鐵素體測試儀典型應(yīng)用領(lǐng)域

測量以下材料內(nèi)的鐵素體含量：

• 雙相鋼  
• 奧氏體焊縫（鋼管或鋼片上）
• 有奧氏體鉻合金鋼焊覆層的普通鋼（鍋爐、容器）

Chemical, energy and processing plants are often
subject to heat, aggressive media and high pressure.
These circumstances demand steel with high corrosion
and acid resistance that are resilient even at high
temperatures. If the ferrite content is too low, then
the welded material is susceptible to hot-cracking, if
the ferrite content is too high, the toughness, ductility
as well as the corrosion resistance of the steel are
reduced. For duplex steel, a ferrite deficit in the area
of the weld seam results in stress corrosion cracking
and reduction in strength.