文獻名: Preparation of cationic fluorinated acrylate copolymer latex and its application on cotton fabric
作者: Yicong Chen, Fujin Fu, Guifang Yang, Yifan Liu, Yuancai Lv & Minghua Liu
Fujian Provincial Engineering Research Center of Rural Waste Recycling Technology, College of Environment and Resources, Fuzhou University, No. 2 Xueyuan Road, Shangjie Town, Minhou County, Fuzhou, 350116, Fujian, China
Fujian Provincial Technology Exploitation Base of Biomass Resources, Fuzhou University, Fuzhou, 350116, China
摘要:Coupled with the improvement in people’s living standards, the demand for textiles having a special performance like water repellency is mushrooming. In this study, the cationic fluorinated acrylate copolymer latex particles with a core–shell structure were synthesized via semicontinuous seed emulsion polymerization process, using Span 80, Tween 80, and dodecyltrimethylammonium chloride as composite emulsifier and (2-(acryloyloxy)ethyl)trimethylammonium chloride as a cationic monomer. Cationic fluorinated acrylate copolymers were successfully confirmed through the FTIR, 1H NMR, and XPS analyses. In addition, the homogeneous latex particles (~ 132 nm of average size) with an evident core–shell structure were observed by TEM analysis, and a stable positive charge (48 ± 5 mV) on the surface of latex particles was demonstrated by zeta potential analysis. Meanwhile, the results showed that the dosage of dodecafluoroheptyl methacrylate (DFMA) played a vital role in the hydrophobicity of the latex films and the one with the best water repellency was identified with 10 g of DFMA dosage. Furthermore, the cotton fabric finishing experiments demonstrated that, after finishing by the cationic fluorinated acrylate copolymer emulsion, the treated cotton fabric exhibited excellent hydrophobicity even at low concentration, with > 130° of the water contact angle and > 60 min of the static absorbing time.
免責聲明
- 凡本網(wǎng)注明“來源:化工儀器網(wǎng)”的所有作品,均為浙江興旺寶明通網(wǎng)絡有限公司-化工儀器網(wǎng)合法擁有版權或有權使用的作品,未經本網(wǎng)授權不得轉載、摘編或利用其它方式使用上述作品。已經本網(wǎng)授權使用作品的,應在授權范圍內使用,并注明“來源:化工儀器網(wǎng)”。違反上述聲明者,本網(wǎng)將追究其相關法律責任。
- 本網(wǎng)轉載并注明自其他來源(非化工儀器網(wǎng))的作品,目的在于傳遞更多信息,并不代表本網(wǎng)贊同其觀點和對其真實性負責,不承擔此類作品侵權行為的直接責任及連帶責任。其他媒體、網(wǎng)站或個人從本網(wǎng)轉載時,必須保留本網(wǎng)注明的作品第一來源,并自負版權等法律責任。
- 如涉及作品內容、版權等問題,請在作品發(fā)表之日起一周內與本網(wǎng)聯(lián)系,否則視為放棄相關權利。