作者: Shaun Ang, Victoria Haritos, Warren Batchelor
Bioresource Processing Research Institute of Australia, Department of Chemical Engineering, Monash University, Melbourne, Victoria 3800, Australia
摘要:The global abundance of recycled pulp has introduced opportunities for cellulose nanofiber (CNF) production at lower energy due to the partially fibrillated nature of recycled pulp. This study investigated the potential of recycled pulp as a feedstock for CNF production, comparing recycled bleached de-inked pulp (DIP) predominantly from eucalyptus fibers with virgin bleached eucalyptus kraft (BEK) pulp. The specific energy consumption for CNF production with 10,000 PFI refiner revolutions and 1 homogenization pass was 7 % lower with recycled pulp. At this treatment level, fiber characterization experiments revealed that the CNF from recycled pulp had a median diameter of 19 nm and aspect ratio was 140, similar to that from virgin pulp. The tensile index of unrefined BEK sheets (30 Nm/g) almost doubled (55 Nm/g) when reinforced with only 20 wt% DIP CNF. This work demonstrates that recycled pulp is a viable alternative to virgin pulp feedstocks for CNF production.
免責聲明
- 凡本網注明“來源:化工儀器網”的所有作品,均為浙江興旺寶明通網絡有限公司-化工儀器網合法擁有版權或有權使用的作品,未經本網授權不得轉載、摘編或利用其它方式使用上述作品。已經本網授權使用作品的,應在授權范圍內使用,并注明“來源:化工儀器網”。違反上述聲明者,本網將追究其相關法律責任。
- 本網轉載并注明自其他來源(非化工儀器網)的作品,目的在于傳遞更多信息,并不代表本網贊同其觀點和對其真實性負責,不承擔此類作品侵權行為的直接責任及連帶責任。其他媒體、網站或個人從本網轉載時,必須保留本網注明的作品第一來源,并自負版權等法律責任。
- 如涉及作品內容、版權等問題,請在作品發(fā)表之日起一周內與本網聯(lián)系,否則視為放棄相關權利。