作者: Liying Wua,b,c, Junming Honga,b,c, Qian Zhanga,b,c, Bor-Yann Chend, Ji Wanga,b,c, Zhengyu Donga,b,c
a Department of Environmental Science and Engineering, Huaqiao University, Xiamen 361021, China
b Xiamen Engineering Research Center of Industrial Wastewater Biochemical Treatment, Xiamen 361021, China
c Fujian Provincial Research Center of Industrial Wastewater Biochemical Treatment (Huaqiao University), Xiamen 361021, China
d Department of Chemical and Materials Engineering, National I-Lan University, 26047, Taiwan
摘要:This first-attempt study explored interactive function of oxygen vacancies, transition metals, and surface hydroxyl groups for persulfate (PS) activation, at different pH conditions. Oxygen vacancy-rich Fe2Co1-LDHs was fabricated via calcination in hydrogen atmosphere. The Fe2Co1-LDH possessed the maximal concentration of oxygen vacancies and abundant hydroxyl groups for effective functioning according to the characterization through X-ray photoelectron spectroscopy (XPS) and electron paramagnetic resonance (EPR). The BPA-degrading efficiency in the LDHs/PS system indicated that Fe2Co1-LDH exhibited the most promising activated performance since oxygen vacancies could improve the catalytic efficiency to enhance electron transport phenomena between the Fe and Co. N2 experiments proved that the presence of oxygen vacancies could promote the production of 1O2 and O2−. Phosphate and pH effect experiments showed the Fe2Co1-LDH/PS system stably maintained operation performance over a wide pH range for bisphenol A (BPA) removal with the effect of surface hydroxyl groups. Practical samples had little effect on the removal of BPA. According to the quenching experiments and EPR technology, SO4− was the main active radicals in acid and neutral conditions and apparently the OH played the crucial role at alkaline pHs. Two different major reaction routes at different pH levels in the Fe2Co1-LDH/PS system for mechanisms of BPA degradation were proposed herein. The Chemical intermediates of BPA degradation were identified by gas chromatography-mass spectrophotometry (GC–MS) analysis, and degradation pathways were proposed for system optimization.
免責聲明
- 凡本網注明“來源:化工儀器網”的所有作品,均為浙江興旺寶明通網絡有限公司-化工儀器網合法擁有版權或有權使用的作品,未經本網授權不得轉載、摘編或利用其它方式使用上述作品。已經本網授權使用作品的,應在授權范圍內使用,并注明“來源:化工儀器網”。違反上述聲明者,本網將追究其相關法律責任。
- 本網轉載并注明自其他來源(非化工儀器網)的作品,目的在于傳遞更多信息,并不代表本網贊同其觀點和對其真實性負責,不承擔此類作品侵權行為的直接責任及連帶責任。其他媒體、網站或個人從本網轉載時,必須保留本網注明的作品第一來源,并自負版權等法律責任。
- 如涉及作品內容、版權等問題,請在作品發(fā)表之日起一周內與本網聯系,否則視為放棄相關權利。