文獻(xiàn)名: Production and characterization of lignin containing nanocellulose from luffa through an acidic deep eutectic solvent treatment and systematic fractionation
作者: Shu Hongab,Yandan Songa, Yang Yuana, Hailan Liana, Henrikki Liimatainenb
a
College of Materials Science and Engineering, Nanjing Forestry University, Nanjing, 210037, China
b
Fibre and Particle Engineering Research Unit, University of Oulu, P.O. Box 4300, FI-90014, Finland
摘要:In this study, lignin and hemicelluloses were partially separated from non-wood biomass of luffa sponge using an acidic deep eutectic solvent (ADES) composed of choline chloride and oxalic acid dihydrate, and the obtained cellulose-rich residue was further disintegrated into lignin containing cellulose nanocrystal (OA-CNC) and nanofiber (OA-CNF) fractions with a two-step ultrasonication treatment. The ADES had a dual purpose: to produce fractions of biomass and to accelerate the nanofibrillation of cellulose. Under optimal reaction conditions (at 90?°C for 150?min), solid fractions with cellulose content of 76.4?wt% (initially 51.8?wt%) and residual lignin content of 10.7?wt% (initially 17.8?wt%) were achieved. Ultrasonication resulted in lignin containing nanocelluloses with a high total yield (59.1?wt% vs. 50.5?wt% from reference 60% sulfuric acid hydrolysis). They consisted mainly of elongated cellulose nanofibers (OA-CNF) with an average diameter of 28?nm. The OA-CNF were further converted to flexible and foldable self-standing films with tensile strength of 134?MPa and elongation at break of 10.6%. This simplified method also presents great potential for using biomass waste (e.g., wheat straw, branches, and sawdust) to produce lignin containing nanocellulose.
相關(guān)產(chǎn)品
免責(zé)聲明
- 凡本網(wǎng)注明“來源:化工儀器網(wǎng)”的所有作品,均為浙江興旺寶明通網(wǎng)絡(luò)有限公司-化工儀器網(wǎng)合法擁有版權(quán)或有權(quán)使用的作品,未經(jīng)本網(wǎng)授權(quán)不得轉(zhuǎn)載、摘編或利用其它方式使用上述作品。已經(jīng)本網(wǎng)授權(quán)使用作品的,應(yīng)在授權(quán)范圍內(nèi)使用,并注明“來源:化工儀器網(wǎng)”。違反上述聲明者,本網(wǎng)將追究其相關(guān)法律責(zé)任。
- 本網(wǎng)轉(zhuǎn)載并注明自其他來源(非化工儀器網(wǎng))的作品,目的在于傳遞更多信息,并不代表本網(wǎng)贊同其觀點和對其真實性負(fù)責(zé),不承擔(dān)此類作品侵權(quán)行為的直接責(zé)任及連帶責(zé)任。其他媒體、網(wǎng)站或個人從本網(wǎng)轉(zhuǎn)載時,必須保留本網(wǎng)注明的作品第一來源,并自負(fù)版權(quán)等法律責(zé)任。
- 如涉及作品內(nèi)容、版權(quán)等問題,請在作品發(fā)表之日起一周內(nèi)與本網(wǎng)聯(lián)系,否則視為放棄相關(guān)權(quán)利。