作者: Wangxia Wang, Nanxun Sun, Zhaosheng Cai, Kaijin Sun, Feng Gu, Yongcan Jin, Huining Xiao
摘要:Cellulose nanomaterials with high yield and desired properties were sustainably produced using a facile recyclable acid treatment (oxalic acid) with mineral acid catalysis at ambient pressure. The resultant nanocellulose was uniform in dimensions (diameter and length distributions) and highly dispersible in the aqueous phase. The nanocellulose with yield up to 33.9%, a zeta potential of -53.9 mV, and 100% volume stability (24 h) was achieved via oxalic acid treatment in conjunction with sulfuric acid addition. The coating of such nanocellulose on paper created a uniform and dense layer on the surface, which lowered Gurley air permeability (i.e., prolonging the time required for air flow from 3.9 to 681.9 s per 100 mL). Moreover, the coated paper showed a complete grease barrier after 48 h and presented easy-cleaning behavior. The approach developed in this work offers an adoptable guidance to design green and sustainable easy-cleaning surfaces. In turn, this approach will provide potential applications of nanocellulose for green based packaging and environmental protection.
免責聲明
- 凡本網(wǎng)注明“來源:化工儀器網(wǎng)”的所有作品,均為浙江興旺寶明通網(wǎng)絡有限公司-化工儀器網(wǎng)合法擁有版權或有權使用的作品,未經(jīng)本網(wǎng)授權不得轉載、摘編或利用其它方式使用上述作品。已經(jīng)本網(wǎng)授權使用作品的,應在授權范圍內(nèi)使用,并注明“來源:化工儀器網(wǎng)”。違反上述聲明者,本網(wǎng)將追究其相關法律責任。
- 本網(wǎng)轉載并注明自其他來源(非化工儀器網(wǎng))的作品,目的在于傳遞更多信息,并不代表本網(wǎng)贊同其觀點和對其真實性負責,不承擔此類作品侵權行為的直接責任及連帶責任。其他媒體、網(wǎng)站或個人從本網(wǎng)轉載時,必須保留本網(wǎng)注明的作品第一來源,并自負版權等法律責任。
- 如涉及作品內(nèi)容、版權等問題,請在作品發(fā)表之日起一周內(nèi)與本網(wǎng)聯(lián)系,否則視為放棄相關權利。