荷貝克HC121600蓄電池12V56AH含稅含運

荷貝克HC121600蓄電池12V56AH含稅含運

HANDLING AND STORAGE Handling: Unless involved in recycling operations, do not breach the casing or empty the contents of the battery. There may be increasing risk of electric shock from strings of connected batteries. Keep containers tightly closed when not in use. If battery case is broken, avoid contact with internal components. Keep away from combustible materials, organic chemicals, reducing substances, metals, strong oxidizers and water. Storage: Store batteries in cool, dry, well-ventilated areas with impervious surfaces. Batteries should also be stored under roof for protection against adverse weather conditions. Separate from incompatible materials. Avoid damage to containers. Keep away from fire, sparks and heat. Keep away from metallic objects could bridge the terminals on a battery and create a dangerous short-circuit. Charging: There is a possible risk of electric shock from charging equipment and from strings of series connected batteries, whether or not being charged. Shut-off power to chargers whenever not in use and before detachment of any circuit connections. Batteries being charged will generate and release flammable hydrogen gas. Charging space must be ventilated. Prohibit smoking and avoid creation of flames and sparks nearby.

裝卸和儲存處理：除非涉及回收作業(yè)，否則不要破壞電池外殼或清空電池的內裝物。可能會有越來越大的風險，電擊由弦的co。 連在一起的電池。不使用時保持容器緊閉。如果電池外殼壞了，避免與內部部件接觸。遠離易燃材料，有機化學品，減少 物質，金屬，強氧化劑和水。儲存：電池存放在陰涼、干燥、通風良好的區(qū)域，表面不透水.電池也應存放在屋檐下，以防止電池損壞。 惡劣天氣條件。與不相容的材料分離。避免對容器造成損壞。遠離火災、火花和熱量。遠離金屬物體可以橋接球棒上的端子 制造危險的短路。充電：無論是否充電，充電設備和串聯(lián)電池串都有可能發(fā)生電擊。什 無論在使用中還是在拆何電路連接之前，都應將電源斷電至充電器。被充電的電池將產生和釋放易燃的氫氣。必須對充電空間進行通風。

EXPOSURE CONTROL / PERSONAL PROTECTION Common Name OSHA PEL ACGIH TLV Range Percent by Weight Negative Electrode and Grid 0.05 mg/m3 0.15 mg/m3 54-62% wt Electrolyte 1.00 mg/m3 1.00 mg/m3 26-40% wt Percentages of components are dependent both on the model of the battery and stets of charge/discharge of the battery. Inorganic lead and electrolyte (sulphuric acid) are the primary components of every battery manufactured by HOPPECKE Batterien GmbH & CO. KG. Other ingredients may be present dependent upon battery type. Contact your HOPPECKE Batterien GmbH & CO. KG representative for additional information. Under normal use and handling the customer has no contact with the internal components of the battery or the chemical hazards. Under normal use and handling these batteries do not emit regulated or hazardous substances. Warning: Battery terminals posts and related accessories contain lead and lead compounds, chemicals known to the State of California to cause cancer and reproductive harm. Wash hands thoroughly after working with batteries and before eating, drinking or smoking.

..曝光控制/個人保護通用名稱OSHA PEL ACGIH TLV按重量計的范圍百分比負極和柵0.05 mg/m3 0.15 mg/m3 54-62%wt電解質1.00 mg/m3 1.00 mg/m3 26-40%wt 組件的百分比既取決于電池的模型，也取決于電池的充放電。 無機鉛和電解質(硫酸) 是 EVE 的主要成分。 RY電池由HOPPECKE Batterien GmbH&CO制造。公斤。其他成分可能取決于電池類型。聯(lián)系您的HOPPECKE Batterien GmbH&CO。kg補充I代表 信息。在正常使用和處理的情況下，客戶沒有接觸到電池的內部部件或化學危害。在正常使用和使用時，這些電池不釋放雷格。  

1.從UPS電源歷史記錄中可查，該UPS電源在電池沒有放電的情況下，突然由浮充轉均充并充電12個小時，導致電池內部溫度突升，殼體變形。
　　
　　2.地下室精密空調之前由于室外機過臟，高壓鎖定停機，缺少了降溫設備導致加速了熱失控的發(fā)生。
　　
　　3.UPS間沒有監(jiān)控設備和負責人員，長期處于無人看管的狀態(tài)。
　　
　　對于此次事故，客戶曾有疑問，懷疑電池膨脹的原因是由于電池排氣閥未能及時打開所致。膨脹變形原因分為熱變形和受力變形，電池殼體承受壓力變形的能力遠大于排氣閥，若出現(xiàn)內部壓力過高，肯定會首先打開排氣閥減少壓力。實際電池膨脹是因為熱變形造成，在熱失控情況下，內部溫度過高造成殼體高溫變形。

　　
　　1.建議使用帶有溫度補償的充電設備，增加電池監(jiān)控設備為上策，以對每一塊電池實時測量性能。
　　
　　2.UPS間室內環(huán)境應通風，溫度維持在20~25°C，配備機房專用空調，以適應長時間不間斷的恒溫需求。
　　
　　3.免維護電池只是維護量相對降低，并非不需維護與保養(yǎng)，在使用中也是需要有人維護。
　　
　　綜合上述，閥控式鉛酸蓄電池熱失控是在外因的誘導下逐步發(fā)生的，因此在使用中對可能造成熱失控的因素要稍加注意，在一定程度上可預防熱失控的出現(xiàn)，保障設備的安全，保障客戶的利益。